Ethylene Vinyl Acetate Polymerization Mechanism

There are three different types of eva copolymer which differ in the vinyl acetate va content and the way the materials are used.

Ethylene vinyl acetate polymerization mechanism.

By this route using mercury ii catalysts vinyl acetate was first prepared by fritz klatte in 1912. In the production of ethylene vinyl acetate copolymers in a free radical catalyst initiated high pressure process explosive decomposition is prevented by contacting the reactor effluent downstream. 12 8 1 ethylene vinyl acetate eva is a copolymer of ethylene and vinyl acetate va segments typically formed via free radical polymerization. Eva copolymers are commercially used predominantly in the areas of coating laminating and in the film industries.

Eva generally contains 1 50 of the va comonomer along the carbon chain backbone. Vinyl acetate was once prepared by hydroesterification. The effects of temperature pressure added co solvent vinyl acetate feed rate and emulsifier type and concentration on the rate of polymerization cumulative copolymer composition molecular. This method involves the gas phase addition of acetic acid to acetylene in the presence of metal catalysts.

The polymerization reaction is initiated by forming alkene metal complex. By fine tuning the ethylene pressure and the vinyl acetate content a broad range of copolymers containing from 0 to 85 mol of vac unit was achieved. Ethylene vinyl acetate eva also known as poly ethylene vinyl acetate peva is the copolymer of ethylene and vinyl acetate the weight percent of vinyl acetate usually varies from 10 to 40 with the remainder being ethylene. Us2703794a us245079a us24507951a us2703794a us 2703794 a us2703794 a us 2703794a us 245079 a us245079 a us 245079a us 24507951 a us24507951 a us 24507951a us 2703794 a us2703794 a us 2703794a authority us united states prior art keywords ethylene vinyl acetate weight copolymer water prior art date 1951 09 04 legal status the legal status is an assumption and is not a legal conclusion.

Coordination copolymerization of vinyl acetate vac with ethylene leading to linear copolymers that possess in chain ch 2 ch oac units has been accomplished using novel palladium complexes bearing alkylphosphine sulfonate ligands. When a vinyl monomer like propylene comes to the active metal center it can be coordinated to ti atom by overlapping their orbitals. A prior extensive experimental phase identified those variables that are most important for ethylene vinyl acetate emulsion copolymer production.